Introduce:
- DELO ML is a group 1- component metal adhesive with high thermal resistance and strength – suitable for electric motor assembly;
- DELO ML allows high thermal resistance, fast curing in anaerobic conditions when contacted to metal ions. DELO ML such as a screw locking adhesive, sealing any thread and surface locking gaps;
- The product is suitable for coaxial metal joints. Using visible light and UV curing glue helps fasteners cure even in hard to reach areas in seconds;
- Ingredients: Modified Urethane acrylate, 1-component glue, solvent-free;
- Operating temperature: - 60 0C ~ +180 0C;
- Compliant RoHS directly 2015/863/EU, and passed anti-flammable test UL 94 HB standard.
Application:
- DELO ML is very flexible, uniform pressure resistance, suitable for metal-glass, metal-plastic joints.
- Applications of DELO ML include:
- Fixation, tightening coaxial connections;
- Screws on materials without drilling
- Mounting pipes, bolts, metal joints
- Glue for the industries of engine manufacturing, automobile assembly, consumer electronics assembly, mechanical engineering
- High strength adhesive for coaxial, rack, or socket mounting.
Some typical applications of DELO-ML glue:
1. Thread locking, vacuum sealing of threaded joints, pipes
Material parts:
Test requirements:
|
2. DELO ML glue is used in fixing bolts of reducer gears
- Thread these bolts with DELO-ML 5327 glue. During operation, screws and adhesives are contacted to the hot oil at temperatures up to +90°C.
Material Composition:
- Bolt: steel
- Gear: cast iron
Vacuum seal for oil level checking screw:
The oil level check screw bonded with DELO-ML 5149 low strength adhesive has a sealing function in this case. When required, it must be possible to remove the screw back.
3. EBM-Papst Electric Car Engine Magnet Bonding
Material Composition:
The requirements and parameters of the glue test passed:
Tests:
|
Dispensing method:
- The bonded surface needs to be clean from dust, grease, recommend DELOTHEN products to get the most perfect surface.
- The adhesive can be easily applied by hand or used in conjunction with DELO's dedicated dispersant - DELOMAT 100, which is compatible with anaerobic curing adhesives.
- The adhesive has a low viscosity, the visible margin of the glue can use light to cure. The adhesive has high strength, is difficult to remove, good adhesion even to surfaces with low roughness.
DELOMAT 100 dispenser
Curing process:
- In an anaerobic environment for several minutes.
- The curing speed of the glue can be increased by heating or using an activator or by UV light with a wavelength from 320 ~ 450 nm for a gap as large as 4 mm.
- Refer to the standard wavelength range of the DELOLUX 20/50/80 LED lamps.
Specifications:
GENERAL TABLE OF TECHNICAL SPECIFICATIONS DELO - ML COMMON APPLICATIONS
Specifications | DELO ML Metal Adhesive (Metal Light) | |||||||
DB133 | DB135 | ML DB140 | DB154 | DB180 | ML 5327 | UB160 | ||
Components | Modified Urethane acrylate | Modified urethane methacrylate ester | ||||||
Color (for 1mm thick cured glue) | Transparent, colorless | Yellowish, transparent | Yellowish, transparent, luminescent | Yellowish, transparent, luminescent | Yellowish, translucent, | Green | Green | |
Density (g/cm 3 ) | 1.1 | 1.1 | 1.09 | 1.1 | 1.1 | 1.1 | 1.1 | |
Viscosity (mPa.s) | 730 | 1200 | 900 | 6000 | 17000 | 300 | 10000 | |
Activator | DELO-QUICK 5002 | DELO-QUICK 5006 | DELO-QUICK 5006 | DELO-QUICK 5002 | - | DELO-QUICK 5002, 5006 | - | |
Temperature range in use ( oC) | -40 ÷ +150 | -60 ÷ +180 | -60 ÷ +180 | -60 ÷ +180 | -60 ÷ +180 | -60 ÷ +200 | -60 ÷ +200 | |
UV suitable wavelength (nm) | 365 nm | 365, 400 nm | 365, 400 nm | 365, 400 nm | 365, 400 nm | - | - | |
UV irradiation time with special intensity (s) | 25s, | 10s, | 10s, | 6s, | - | - | - | |
Initial curing time (tensile shear strength 1~2 MPa) | 3 ~ 6 min | 2 ~ 4 min | 1 ~ 3 min | 2 ~ 4 min | - | 2 ~ 4 min | 2 ~ 4 min | |
Final curing time | 24h | 24h | 24h | 24h | - | 20 min |
| |
Off-torque (Nm) | No momen | 30 Nm | 30 Nm | - | 34 Nm | 60 Nm | 50 Nm | 40 Nm |
Momen M=46 Nm | - | 60 Nm | - | 65 Nm | - | 70 Nm | 70 Nm | |
Compression shear strength (MPa) | Glass/ glass | 30 | 30 | 30 | 11 | 16 | - | - |
PA6/ Stainless steel | 10 | 10 | - | 6 | 10 | - | - | |
PA6 / PA6 | 18 | 16 | - | 7 | 15 | - | - | |
Steel shaft/ steel hub | 28 | - | 40 | 35 | 40 | 33 | 40 | |
Tensile shear strength (MPa) | Al/Al (sandblasted, cured for 72h) | 12 | 13 | 6 | 13 | 13 | 11 | 8 |
Steel/Steel (sandblasted, sau 72h) | 14 | 16 | 13 | 16 | 14 | 16 | 14 | |
Tensile strength (MPa) | 20 | 30 | - | 60 | 30 | - | - | |
Elongation at tear (%) | 130 | 30 | 30 | 4 | 35 | - | - | |
Young's modulus (MPa) | 300 | 900 | 900 | 3000 | 1000 | - | - | |
Shore hardness | D 44 | D 70 | D 74 | D 84 | D 70 | - | - | |
Glass transition temperature ( o C) | 104 oC | 110 oC | 120 oC | 110 oC | 90 oC | - | 133 oC | |
Coefficient of thermal expansion (ppm/K) | 100~150oC: 184 ppm/K | 95 – 150oC: 203 ppm/K | 100–160oC: 179 ppm/K | - | 30-150oC: 195 ppm/K | - | - | |
Shrinkage (%vol.) | 8.6 | 7.7 | 8.7 | 8.4 | 7.8 | - | - | |
Water absorption (%wt) | - | 1.03 | 0.8 | 0.7 | 1.1 | - | - | |
Volumetric Resistance (Ohm.cm) | 1x1016 | 3x1016 | - | - | - | - | - | |
Surface Resistance (Ohm) | 1x1014 | 2x1014 | - | - | - | - | - | |
Storage (with an unopened container) | 9 months at 0-10 o C, 6 months at 25 ° C | 6 months at 0-10 o C, 3 months at 25 ° C | 6 months at 0-10 o C, 3 months at 25 ° C | 6 months at 25 ° C | 6 months at 0-10 o C, 6 months at 25 ° C (for bottle≤900ml) | 12 months at 0-10 o C, 6 months at 25 ° C | 6 months at 25 ° C (for bottle≤600ml) (glue lifetime 4 weeks after opening) |
For more detailed information, please contact us.