Introduce:
- It is a transparent, solvent-free, low-viscosity, flowable, modified epoxy adhesive with fully curing by light.
- Halogen-free according to IEC 61249-2-21;
- Compliant RoHS 2015/863/EU standard.
- Specialized in bonding optical materials, imprint materials.
Application:
- Specialized in optical materials such as lenses in replicative processing.
- Bonds temperature-sensitive materials.
Curing:
Suitable wavelength: | 365 nm |
UV intensity: | 200 mW/cm2 |
Irradiation time: | 30 s |
Specifications:
Processing | ||
Typical dispensing | Needle dispensing | |
Defrost waiting time | 1 hour for glue cartridge ≤ 50 ml | |
Heat annealing time (helps increase transparency) | 1 hour at 120 o C | |
Wait time for cooling the mold after annealing: | Mandatory to avoid cracking for demolding | |
Technical parameters | ||
Colour: | Colorless, transparent | |
Density: | 1.13 g/cm3 | |
Viscosity (at 23 ° C, Rheometer measurement, speed 10 1/s): | 400 mPas | |
Maximum cured glue thickness: | 4 mm | |
Compression shear strength | glass/glass | 20 MPa |
glass/PC | 12 MPa | |
Glass/Al | 20 MPa | |
Tensile strength: | 23 MPa | |
Elongation at tear: | 70 % | |
Young's modulus: | 800 MPa | |
Shore D hardness: | 60 | |
Glass transition temperature: | 410C | |
Decomposition temperature: | 2860C | |
Coefficient of thermal expansion | Range -40 ~ 0 o C | 91 ppm/K |
Range 90 ~ 170 o C | 207 ppm/K | |
Shrinkage: | 2.6 % vol. | |
Water Absorption: | 0.9 % wt. | |
Số Abbe (Refractometer): | 55 | |
Shelf life (with unopened container): | - 6 months at 0 ~ 25 0 C - 9 months at 0~10 o C |
For more detailed information, please contact us.